Durethan® BKV 15 H3.0 DUS008 000000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xrZFuo_Durethan-BKV-15-H3-0-DUS008-000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 15 % glass fibers, injection molding, heat-aging stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.23 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 2577 | |||
| Across Flow : 280°C, 3.00 mm 1 | 0.60 | -- | % | |
| Across Flow : 120°C, 4 hr, 3.00 mm 2 | 0.15 | -- | % | |
| Flow : 280°C, 3.00 mm 3 | 0.35 | -- | % | |
| Flow : 120°C, 4 hr, 3.00 mm 4 | 0.15 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 6500 | 3100 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 130 | 65.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.0 | 12 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 5500 | 3100 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | |||
| 3.5% Strain, 23°C | 180 | 80.0 | MPa | |
| 23°C 6 | 205 | 110 | MPa | |
| Flexural Strain at Flexural Strength 7(23°C) | 5.3 | 8.0 | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA6, GHR, 14-070, GF15 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 45 | 45 | kJ/m² | |
| 23°C | 50 | 100 | kJ/m² | |
| Notched Izod Impact Strength (23°C) | < 10 | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 40 | 40 | kJ/m² | |
| 23°C | 45 | 85 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 195 | -- | °C | ISO 75-2/A |
| Melting Temperature 8 | 220 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 3.0E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 1.0E-4 | -- | cm/cm/°C |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 150x105x3mm, 80°C MT, 500 bar |
| 2 . | 150x105x3mm |
| 3 . | 150x105x3mm, 80°C MT, 500 bar |
| 4 . | 150x105x3mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Witcom PPS 6C/3L1-L | Witcom Engineering Plastics B.V. | PPS | Witcom PPS |
| Network Polymers SMMA MS 200 | Network Polymers, Inc. | Acrylic (SMMA) | Network Polymers SMMA |
| Axiall PVC 19481 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Hostalen CRP 100 S brown | LyondellBasell Industries | HDPE | Hostalen |
| LNP™ THERMOCOMP™ RF00AH compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |