ATTANE™ 4404G
| Category: | ULDPE , Ultra Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ATTANE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xrR2BG_ATTANE-4404G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.904 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Puncture Resistance | Internal method | ||
| 20 µm | 18.9 | J/cm³ | Internal method |
| 51 µm | 17.5 | J/cm³ | Internal method |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 20 µm | 58.8 | MPa | ASTM D882 |
| 2% secant, MD : 51 µm | 62.6 | MPa | ASTM D882 |
| 2% secant, TD : 20 µm | 64.7 | MPa | ASTM D882 |
| 2% secant, TD : 51 µm | 63.0 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 20 µm | 7.00 | MPa | ASTM D882 |
| MD : Yield, 51 µm | 6.76 | MPa | ASTM D882 |
| TD : Yield, 20 µm | 4.92 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 6.34 | MPa | ASTM D882 |
| MD : Break, 20 µm | 36.9 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 32.6 | MPa | ASTM D882 |
| TD : Break, 20 µm | 29.1 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 32.4 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 20 µm | 500 | % | ASTM D882 |
| MD : Fracture, 51 µm | 660 | % | ASTM D882 |
| TD : Break, 20 µm | 710 | % | ASTM D882 |
| TD : Fracture, 51 µm | 710 | % | ASTM D882 |
| Dart Drop Impact | ASTM D1709B | ||
| 20 µm | > 850 | g | ASTM D1709B |
| 51 µm | > 850 | g | ASTM D1709B |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 20 µm | 330 | g | ASTM D1922 |
| MD : 51 µm | 960 | g | ASTM D1922 |
| TD : 20 µm | 500 | g | ASTM D1922 |
| TD : 51 µm | 1100 | g | ASTM D1922 |
| Oxygen Permeability (23°C, 51 µm) | 450 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate (51 µm) | 0.85 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Carbon Dioxide Transmission Rate (23°C, 50.8 µm) | 2000 | cm³·mm/m²/atm/24 hr | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 71.1 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 124 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 45°, 20.3 µm | 92 | ASTM D2457 | |
| 45°, 50.8 µm | 90 | ASTM D2457 | |
| Clarity | ASTM D1746 | ||
| 20.3 µm | 99.0 | ASTM D1746 | |
| 50.8 µm | 99.0 | ASTM D1746 | |
| Haze | ASTM D1003 | ||
| 20.3 µm | 0.60 | % | ASTM D1003 |
| 50.8 µm | 1.8 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| 铸造薄膜的制造条件： 模具间隙：25 密尔 (2 mm) 冷却辊温度：70°F (21°C) 生产线速度：200 fpm（61 米/分） |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME Specialty PS SP06425 9885 | Supreme Petrochem Ltd. | PS (HIPS) | SUPREME Specialty PS |
| Nymax™ GF1200 A30 FR BL286 | PolyOne Corporation | Nylon 66 | Nymax™ |
| KYDEX® FST CTL | SEKISUI Polymer Innovations, LLC | PMMA+PVC | KYDEX® |
| INVISION™ HX 5145DU1A | A. Schulman Inc. | TPE | INVISION™ |
| LIHAN® B100 | Nanjing Lihan Chemical Co., Ltd. | Nylon 6 | LIHAN® |