Order Products : sales@su-jiao.com
GETILAN ATP/190 3AP
| Category: | XLPE , Crosslinked Polyethylene |
| Manufacturer: | Crosspolimeri S.p.A. |
| Trademark: | GETILAN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xqDoel_GETILAN-ATP-190-3AP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GETILAN ATP/190 3AP is a crosslinkable (SIOPLAS technology) polyolefinic compound. GETILAN ATP/190 3AP is a high density antiflame chemically crosslinkable polythene with high temperature index and low HCl content. Suitable for automotive cables insulation. It is a conveniently grafted polythene able to react in presence of moisture and of catalyst. We normally suggest our catalyst type MAC/203 HS or MAC/203 HSL (less reactive). REACTION BETWEEN GRAFTING AND CATALYST: These two polythenes, separately stored, must be mixed before starting extrusion in the ratio: GRAFTING/CATALYST 96/4 Certify: SAE J1127/J1128,FIAT 7.Z8220 T3 -T3 S,ISO 6722 Class C,LV 112 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 18 - 25 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 59 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | > 14.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 200 | % | ASTM D638 |
| Aging | Nominal Value | Test Method | |
|---|---|---|---|
| Heat Aging | IEC 60811 | ||
| 240 hr : 150°C | No Crack | IEC 60811 | |
| 6 hr : 175°C | Pass | IEC 60811 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Service Temperature | -40 - 125 | °C | |
| Thermoset 1 | IEC 60811 | ||
| 200°C | 50 | % | IEC 60811 |
| Residual : 200°C | % | IEC 60811 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Halogen Content | % | IEC 60754-1 | |
| Oxygen Index | 26 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 150 | °C | |
| Cylinder Zone 2 Temp. | 170 | °C | |
| Cylinder Zone 3 Temp. | 190 | °C | |
| Cylinder Zone 4 Temp. | 200 | °C | |
| Cylinder Zone 5 Temp. | 220 | °C | |
| Die Temperature | 235 | °C |
| Extrusion instructions |
|---|
| CROSSLINKING:Crosslinking of the finished product is obtained by: Immersion of the bobbin into hot water at 85/90°C for two hours (up to 3 mm thickness). Steam treatment at 0.15 for bar 5/6 hours. Faster ambient curing is possible depending from the atmospheric conditions. |
| Note Message | |
|---|---|
| 1 . | 20 N/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TABOND 5007 | SILON s.ro | PP, Unspecified | TABOND |
| VALOX™ VX5011 resin | SABIC Innovative Plastics Europe | PBT | VALOX™ |
| Aaroprene® TFIPP 2010 | Aaron Industries Corp. | PP, Unspecified | Aaroprene® |
| AVALON® 85 ABU | Huntsman Corporation | TPU-Polyester | AVALON® |
| KumhoSunny ABS 760 | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | KumhoSunny ABS |