Styrolution PS 1900
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | INEOS Styrolution Group GmbH |
| Trademark: | Styrolution PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xp1LHq_Styrolution-PS-1900.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Styrolution PS 1900 is a General Purpose Polystyrene product. It can be processed by foam extrusion or injection molding and is available in Latin America or North America. Applications of Styrolution PS 1900 include additive/masterbatch and foam. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Apparent Density 1 | 0.59 to 0.64 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 23 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 74 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2960 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 34.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.0 | % | ASTM D638 |
| Flexural Modulus | 3310 | MPa | ASTM D790 |
| Flexural Strength | 68.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 16 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 96.1 | °C | |
| Vicat Softening Temperature | 105 | °C | ASTM D1525 2 |
| CLTE - Flow | 7.2E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (3.18 mm) | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1.00 mm, 1 MHz) | 2.50 | ASTM D150 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index 3 | 1.590 | ASTM D542 | |
| Transmittance (550 nm) | 88.0 to 90.0 | % | ASTM D1003 |
| Optical Density - 400-700 nm avg. | 0.0460 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 191 to 274 | °C | |
| Mold Temperature | 37.8 to 82.2 | °C |
| Note Message | |
|---|---|
| 1 . | without external lubricant |
| 2 . | Rate B (120°C/h), Loading 1 (10 N) |
| 3 . | Sodium D line |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shanghai Potomer SG2 | Shanghai Potomer International Trade Co., Ltd. | PVC, Flexible | Shanghai Potomer |
| Shandong Nylon A4TR02 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon, Unspecified | Shandong Nylon |
| Spartech Polycom SC5-2220 | Spartech Polycom | PP Copolymer | Spartech |
| DURACON® M25LV | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | DURACON® |
| HI-ZEX™ 7800M | Prime Polymer Co., Ltd. | HDPE | HI-ZEX™ |