Order Products : sales@su-jiao.com
TOTAL Polyethylene LDPE LD 0304
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xny7HC_TOTAL-Polyethylene-LDPE-LD-0304.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LDPE LD 0304 is a low density polyethylene made by a high pressure autoclave process without antioxidant. Application examples: coating of paper, paperboard, aluminium, ... |
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | |||
| -- | 0.924 | g/cm³ | ISO 1183 |
| -- | 923 | kg/m³ | ISO 1183 1 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Melt volume-flow rate (190°C/2.16 kg) | 5.50 | cm³/10min | ISO 1133 2 |
| Water Absorption (Saturation) | 0.010 | % | ISO 62 3 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- | 250 | MPa | ISO 527-2 |
| -- | 220 | MPa | ISO 527-2 4 |
| Tensile Stress | |||
| Yield | 11.0 | MPa | ISO 527-2 |
| Fracture | 13.0 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Yield | 15 | % | ISO 527-2 5 |
| Fracture | 550 | % | ISO 527-2 |
| Tensile Elongation at Break | > 50 | % | ISO 527-2 6 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 95.0 | °C | ISO 306 |
| 50°C/h, B (50N) | 94.0 | °C | ISO 306 7 |
| Melting Temperature (DSC) | |||
| -- | 111 | °C | ISO 3146 |
| -- 8 | 112 | °C | ISO 11357-3 9 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 10 |
| Volume Resistivity | > 1.0E+13 | ohms·m | IEC 60093 11 |
| Relative Permittivity (100 Hz) | 2.00 | IEC 60250 12 | |
| Dissipation Factor | IEC 60250 13 | ||
| 100 Hz | 2.0E-4 | IEC 60250 | |
| 1 MHz | 2.0E-4 | IEC 60250 | |
| Comparative Tracking Index | 600 | IEC 60112 14 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Behav. at 1.6mm nom. thickn. (1.60 mm) | HB | ISO 1210 15 | |
| Oxygen Index | 18 | % | ISO 4589-2 16 |
| Additional Information |
|---|
| The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 200 - 320 | °C | |
| Cylinder Zone 2 Temp. | 200 - 320 | °C | |
| Cylinder Zone 3 Temp. | 200 - 320 | °C | |
| Cylinder Zone 4 Temp. | 200 - 320 | °C | |
| Cylinder Zone 5 Temp. | 200 - 320 | °C | |
| Die Temperature | 260 - 320 | °C |
| Note Message | |
|---|---|
| 1 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 2 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 3 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 4 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 5 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 6 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 7 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 8 . | 10 °C/min |
| 9 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 10 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 11 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 12 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 13 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 14 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 15 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 16 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2583 FR | RTP Company | PC+ABS | RTP |
| Zythane® 6070A | Alliance Polymers & Services | TPU-Polyether | Zythane® |
| BMC 605LS | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| Evermore PUR SA-2018MP | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| Halene L 72307E | Haldia Petrochemicals Ltd. | LLDPE | Halene L |
