Order Products : sales@su-jiao.com
Tufpet PBT G1020
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Mitsubishi Rayon America Inc. |
| Trademark: | Tufpet |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xnhuBM_Tufpet-PBT-G1020.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Tufpet PBT G1020 is a Polybutylene Terephthalate (PBT) material filled with 20% glass fiber. It is available in North America for injection molding. Important attributes of Tufpet PBT G1020 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.25 to 1.3 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 108 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.1 | % | ASTM D638 |
| Flexural Modulus | 6860 | MPa | ASTM D790 |
| Flexural Strength | 177 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 69 | J/m | ASTM D256 |
| Unnotched Izod Impact | 390 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 204 | °C | ASTM D648 |
| RTI Elec | UL 746 | ||
| 0.760 mm | 75.0 | °C | |
| 1.57 mm | 75.0 | °C | |
| 3.18 mm | 75.0 | °C | |
| RTI Imp | UL 746 | ||
| 0.760 mm | 75.0 | °C | |
| 1.57 mm | 75.0 | °C | |
| 3.18 mm | 75.0 | °C | |
| RTI Str | UL 746 | ||
| 0.760 mm | 75.0 | °C | |
| 1.57 mm | 75.0 | °C | |
| 3.18 mm | 75.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.760 mm | HB | ||
| 1.57 mm | HB | ||
| 3.18 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 230 to 303 | °C | |
| Middle Temperature | 230 to 303 | °C | |
| Front Temperature | 230 to 303 | °C | |
| Mold Temperature | 40.0 to 100 | °C | |
| Injection Pressure | 81.4 | MPa | |
| Screw Speed | 80 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6600 MR 409 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| Ecomann® PHA EM10000 | Shenzhen Ecomann Biotechnology Co., Ltd. | PHA | Ecomann® |
| Globalene® 8681 | Lee Chang Yung Chemical Industry Corp. | PP Random Copolymer | Globalene® |
| POLYblend PC/ABS 45FS GK25 | Polykemi AB | PC+ABS | POLYblend |
| FRIANYL® XT6 GF30 VOXI | Nilit Plastics | PPA | FRIANYL® |