MAJORIS DG304X
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xnTdIv_MAJORIS-DG304X.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAJORIS DG304X is a high performance reinforced polypropylene compound intended for injection moulding. The product is available in natural, but other colours can be provided on request. MAJORIS DG304X has been developed especially for demanding applications in automotive industry and various engineering sectors. MAJORIS DG304X has very high rigidity, good dimensional stability and good creep resistancy also at high temperatures. APPLICATIONS Product requiring high service temperature and extremely high mechanical strength. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Vertical flow direction : 2.00mm | 1.0 | % | |
| Flow direction : 2.00mm | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7900 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 105 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 3.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 6700 | MPa | ISO 178 |
| Flexural Stress | 145 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 8.0 | kJ/m² | ISO 179/1eA |
| 23°C | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 43 | kJ/m² | ISO 179/1eU |
| 23°C | 47 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 152 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 149 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 138 | °C | ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 40.0 - 80.0 | °C | |
| Processing (Melt) Temp | 230 - 270 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C | |
| Injection Rate | Moderate | ||
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Back pressure: as low as possibleScrew speed: Low to medium |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Dynaprene® VE3080A | Nantex Industry Co., Ltd. | TPE | Dynaprene® |
| Karina MBU BLUE -E 06/948-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ DX05477 compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |
| Mediprene® 500352M | ELASTO | SEBS | Mediprene® |
| Sylvin 916VO Brown 7415 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |