SABIC® PPcompound 3020B
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xnR8D7_SABIC-PPcompound-3020B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 3020B is a 20% talc-filled Polypropylene. The material's high modulus and it's thermal and UV stabilization makes it suitable for exterior applications, like cowl top panels. SABIC® PPcompound 3020B is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 1.1 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 72 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/5/50 | ||
| Yield, 3.20 mm, Injection Molded | 29.0 | MPa | |
| Break, 3.20 mm, Injection Molded | 27.0 | MPa | |
| Tensile Strain (Break, 3.20 mm, Injection Molded) | 30 | % | ISO 527-2/5/50 |
| Flexural Modulus 1(Injection Molded) | 2500 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 4.4 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact Strength | ISO 180/4A | ||
| -20°C, Injection Molded | 2.2 | kJ/m² | |
| 0°C, Injection Molded | 2.7 | kJ/m² | |
| 23°C, Injection Molded | 3.1 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 120 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 150 | °C | ISO 306/A |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 5.0E-5 | cm/cm/°C | |
| 23 to 80°C | 1.0E-4 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ MX5210-0040 RS Natural | PolyOne Corporation | PP Homopolymer | Maxxam™ |
| RTP 4001 TFE 13 | RTP Company | PPA | RTP |
| MTEGRITY™ PS General Purpose GS230 | M. Holland Company | PS (GPPS) | MTEGRITY™ PS General Purpose |
| Next Nylon 6 Prime Series NGM30-01GY | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Prime Series |
| Rotuba CAP CP808-12H-22034 Smoke (12% Plasticizer) | Rotuba Extruders, Inc. | CAP | Rotuba CAP |