DOMAMID® 6G20
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DOMO Engineering Plastics SPA |
| Trademark: | DOMAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xnIWTy_DOMAMID-6G20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6, 20% glass fiber reinforced, for injection moulding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.27 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 2577 | |||
| Across Flow : 23°C, 72 hr | 0.80 to 1.0 | -- | % | |
| Flow : 23°C, 72 hr | 0.40 to 0.60 | -- | % | |
| Viscosity Number | 145 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 7100 | 4300 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 145 | 85.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.5 | 7.0 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 6200 | -- | MPa | ISO 178 |
| Flexural Stress 3 | 200 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | 20 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 65 | 85 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | 9.0 | 19 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 60 | 80 | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 195 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 210 | -- | °C | ISO 306/B50 |
| Melting Temperature | 222 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (1.00 to 3.00 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 95.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50% RH |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DOW™ LDPE 722S | The Dow Chemical Company | LDPE | DOW™ LDPE |
| 3M™ Dyneon™ TFM™ Modified PTFE TFM 1635 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE |
| Ad-Tech Epoxy EL-335 | Ad-Tech Plastic Systems Corp. | Epoxy | Ad-Tech Epoxy |
| Delrin® 100TL NC010 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| Envir® PA66T2HL-BK0603 | Barnet | Nylon 66 | Envir® |