Polypropylene homopolymer, 30% chemically coupled fibber glass reinforced compound.
ISPLEN® PG370 AT shows a very high stiffness, keeping good impact strength at every range of temperatures. It also shows a low warpage and shrinkage behaviour. The product is high heat stabilised.

APPLICATIONS

Automotive: Under the bonnet parts subjected to severe mechanical stresses (Light housings, heat and ventilation housings, filters)

Technical pieces, in general.

Electrical housings, power tools.

Washing machines cylinders.

General Information
Filler / Reinforcement	Glass Fiber, 30% Filler by Weight
Additive	Heat Stabilizer
Features	Chemically Coupled Good Impact Resistance Heat Stabilized High Stiffness Low Shrinkage Low Warpage
Uses	Automotive Applications Automotive Under the Hood Electrical Housing Engineering Parts Power/Other Tools White Goods & Small Appliances

Physical	Nominal Value	Unit	Test Method
Density	1.14	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	13	g/10 min	ISO 1133
Molding Shrinkage ¹	0.30 to 0.60	%	ISO 2577

Hardness	Nominal Value	Unit	Test Method
Shore Hardness (Shore D, 15 sec)	78		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Break)	88.0	MPa	ISO 527-2
Tensile Strain (Break)	4.0	%	ISO 527-2
Flexural Modulus	5800	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact Strength			ISO 180
0°C	8.0	kJ/m²
23°C	10	kJ/m²
Unnotched Izod Impact Strength			ISO 180
0°C	45	kJ/m²
23°C	55	kJ/m²

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	158	°C	ISO 75-2/B
1.8 MPa, Unannealed	140	°C	ISO 75-2/A
Vicat Softening Temperature
--	163	°C	ISO 306/A120
--	133	°C	ISO 306/B120

Note Message
1 .	150x100x3mm

Resin Grade	Manufacturer	Category	Trademark
RTP 203 GB 10 TFE 13 SI2	RTP Company	Nylon 66	RTP
Sorona® MT3401 NC010	DuPont Performance Polymers	PTT	Sorona®
NEXUS ABS ABS3030	Nexus Resin Group, LLC.	ABS	NEXUS ABS
Braskem PP R352-08R	Braskem Europe GmbH	PP Random Copolymer	Braskem PP
LG ASA LI918	LG Chem Ltd.	ASA	LG ASA