AKROMID® T1 ICF 20 black (5147)
| Category: | PPA , Polyphthalamide |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xltYGC_AKROMID-T1-ICF-20-black-5147-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® T1 ICF 20 black (5147) is a 20% carbon fibre reinforced polyphthalamid with high flexural strength and good sliding properties Applications are mechanically high stressed parts in all industries |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.25 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 40.0 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.64 | -- | % | |
| Flow | 0.22 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 1.5 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flexural Strain at Break 1 | 2.0 | 2.0 | % | ISO 178 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 20 | -- | % | ISO 1172 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 18000 | 17500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 200 | 200 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.5 | 1.5 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 17000 | 16200 | MPa | ISO 178 |
| Flexural Stress 3 | 300 | 300 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 35 | 30 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melting Temperature 4 | 313 | -- | °C | DIN EN 11357-1 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+5 | 1.0E+5 | ohms | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10 K/min, DSC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEFTEKHIM PE 4052U (52411) | Nizhnekamskneftekhim Inc. | HDPE | NEFTEKHIM PE |
| Arnite® T06 202 | DSM Engineering Plastics | PBT | Arnite® |
| EchoShield R7010 | DN Plastics | TPO (POE) | EchoShield |
| Elastron® G G100.A75.N | Elastron USA, Inc. | SEBS | Elastron® G |
| Geon™ Vinyl Rigid Extrusion L7100 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |