Ultramid® A3WG7 HR BK23591
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xlk5Sc_UltramidA3WG7HRBK23591.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ultramid A3WG7 HR BK23591 is a 35% glass fiber reinforced, heat stabilized, pigmented black, injection molding PA66 for hydrolysis resistant applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 5.0 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.6 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 11400 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 205 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.1 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 11000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 306 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 9.9 | kJ/m² | ISO 179 |
| 23°C | 12 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 72 | kJ/m² | ISO 179 |
| 23°C | 89 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 12 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 250 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 260 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 280 - 305 | °C | |
| Mold Temperature | 80 - 90 | °C | |
| Injection Pressure | 3.50 - 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MegaCarb® 500-FR2 | Mega Polymers | PC | MegaCarb® |
| STERLENE™ CMV207E | R&P (Pte.) Ltd. | TPO (POE) | STERLENE™ |
| Witcom POM-C EC-EP-HI | Witcom Engineering Plastics B.V. | Acetal (POM) Copolymer | Witcom POM-C |
| DENILUB B 20G 3TF | Vamp Tech | PBT | DENILUB |
| POLYFLAM® RPP 1058X | A. Schulman Inc. | PP, Unspecified | POLYFLAM® |