Boda BDF601P
| Category: | Fluorelastomer , Fluoroelastomer |
| Manufacturer: | Chenguang Fluoro & Silicone Elastomers Co., Ltd. |
| Trademark: | Boda |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xlYqaM_Boda-BDF601P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BDF601P is a medium to high viscosity curative incorporated fluoroelastomer copolymer. This grade is well suited for application where good mechanical properties and excellent compression set resistance are required. BDF601P can be compounded to meet the major fluoroelastomer specifications. BDF601P can be used for compression molding of O-rings and gaskets. It can be mixed using typical fluoroelastomer compounding ingredients. Mixing can be accomplished with two-roll mills or internal mixers. Finished goods can be produced by a variety of rubber processing methods. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.82 | g/cm³ | |
| Mooney Viscosity (ML 1+10, 121°C) | 60 | MU | |
| Fluorine Content | 66 | % | |
| Solubility | LMW Ketones and esters |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| MH 1(177°C) | 2.60 | N·m | |
| ML 2(177°C) | 0.500 | N·m | |
| t'90 3(177°C) | 2.3 | min | |
| ts2 4(177°C) | 1.2 | min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 5(Shore A) | 78 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 6(Yield) | 14.5 | MPa | ASTM D412 |
| Tensile Elongation 7(Break) | 180 | % | ASTM D412 |
| Compression Set (200°C, 70 hr) | 13 | % | ASTM D395B |
| Additional Information |
|---|
| Test Compound: Polymer: 100 MT Black (N990): 30 phr MgO: 3 phr Ca(OH)2: 6 phr Curing Condition: Press: 10 min at 170°C Oven: 24 hr at 230°C |
| Note Message | |
|---|---|
| 1 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 2 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 3 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 4 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 5 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| 6 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| 7 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SolVin 460SL | INOVYN | PVC, Unspecified | SolVin |
| Texalan® 6 Series 698A | Austin Novel Materials Co. Ltd. | TPU-Ester/Ether | Texalan® 6 Series |
| Edgetek™ ET3200-0040 RS Black | PolyOne Corporation | PC | Edgetek™ |
| Hysun® A3525 | Ravago Manufacturing Americas, LLC | ASA+PC | Hysun® |
| MACOMASS TPE MM-TPE-V 5031, R1690 | MACOMASS Verkaufs AG | TPE | MACOMASS TPE |