PLANAC BT-1500
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | TOYOBO America, Inc. |
| Trademark: | PLANAC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xktcp1_PLANAC-BT-1500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PLANAC BT-1500 is a polybutene terephthalate (PBT) product,. It can be processed by film extrusion or injection molding and is available in North America or Asia Pacific. Typical application areas are: movies. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.5 | % | ASTM D955 |
| Transverse flow | 1.9 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.080 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 117 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2700 | MPa | ASTM D638 |
| Tensile Strength | 60.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 300 | % | ASTM D638 |
| Flexural Modulus | 2300 | MPa | ASTM D790 |
| Flexural Strength | 90.0 | MPa | ASTM D790 |
| Compressive Strength | 84.0 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 50 | J/m | ASTM D256 |
| Unnotched Izod Impact | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 160 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 70.0 | °C | ASTM D648 |
| CLTE - Flow (-30 to 100°C) | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm) | 26 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.30 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.020 | ASTM D150 | |
| Arc Resistance | 130 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 600 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Additional Information |
|---|
| The value shown for Comparative Track Index, UL 746, was tested in accordance with ASTM D3638.Flexural Elongation @ Break, ASTM D790: NB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 230 - 260 | °C | |
| Middle Temperature | 230 - 260 | °C | |
| Front Temperature | 230 - 260 | °C | |
| Mold Temperature | 20.0 - 70.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MTEGRITY™ PP Homopolymer PP500 | M. Holland Company | PP Homopolymer | MTEGRITY™ PP Homopolymer |
| TRISTAR® PC-10R-(V15) | Polymer Technology and Services, LLC | PC | TRISTAR® |
| Elastocon® OF70B | Elastocon TPE Technologies | TPE | Elastocon® |
| Kepital® FU2020 LOF | KEP Americas | Acetal (POM) Copolymer | Kepital® |
| Sylvin 9077-85 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |