Fortron® FX4382T1
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Celanese Corporation |
| Trademark: | Fortron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xko7mv_Fortron-FX4382T1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Fortron FX4382T1 is an impact-modified, unreinforced, extrusion grade offering high tensile elongation. Recommended processing conditions are identical to our standard unfilled grades. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.26 | g/cm³ | ASTM D792 |
| -- | 1.28 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.70 - 1.4 | % | ISO 294-4 |
| Flow direction | 0.90 - 1.4 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.035 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 41 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -40°C | 3410 | MPa | ASTM D638 |
| 23°C | 2410 | MPa | ASTM D638 |
| 121°C | 345 | MPa | ASTM D638 |
| 200°C | 138 | MPa | ASTM D638 |
| -- | 2800 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield, -40°C | 86.9 | MPa | ASTM D638 |
| Yield, 23°C | 53.9 | MPa | ASTM D638 |
| Yield, 121°C | 12.6 | MPa | ASTM D638 |
| Fracture | 50.0 | MPa | ISO 527-2/1A/5 |
| Tensile Elongation | |||
| Yield, -40°C | 6.0 | % | ASTM D638 |
| Yield, 23°C | 6.0 | % | ASTM D638 |
| Yield, 121°C | 30 | % | ASTM D638 |
| Fracture, -40°C | 10 | % | ASTM D638 |
| Fracture, 23°C | 25 | % | ASTM D638 |
| Fracture, 121°C | 95 | % | ASTM D638 |
| Fracture, 204°C | 96 | % | ASTM D638 |
| Fracture | 25 | % | ISO 527-2/1A/5 |
| Coefficient of Friction (vs. Steel - Dynamic) | 0.20 | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 30 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 81.7 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 100 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 7.7E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 5.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Constant (1.00 GHz) | 3.30 | ASTM D150 | |
| Comparative Tracking Index | 150 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 100 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Hopper Temperature | 20.0 - 30.0 | °C | |
| Rear Temperature | 290 - 300 | °C | |
| Middle Temperature | 300 - 310 | °C | |
| Front Temperature | 310 - 320 | °C | |
| Nozzle Temperature | 300 - 310 | °C | |
| Processing (Melt) Temp | 310 - 320 | °C | |
| Mold Temperature | 140 - 160 | °C | |
| Injection Pressure | 40.0 - 80.0 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 30.0 - 60.0 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 310 to 320°CZone 4 Temperature: 310 to 320°CFeed Temperature: 60 to 80°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8437-76 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| WEVO-CHEMIE Polyurethanes PD 4/385 | WEVO-CHEMIE GmbH | PUR, Unspecified | WEVO-CHEMIE Polyurethanes |
| Nymax™ 1280 A HS Black 11 A | PolyOne Corporation | Nylon 66 | Nymax™ |
| Karina BLUE COLOR CONCENTRATE 06/213-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| KMI PP KM-169IB | KMI Group, Inc. | PP Impact Copolymer | KMI PP |