CoolPoly® E3607
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | CoolPoly® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xkGwrB_CoolPoly-E3607.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CoolPoly E series of thermally conductive plastics transfers heat, a characteristic previously unavailable in injection molding grade polymers. CoolPoly is lightweight, netshape moldable and allows design freedom in applications previously restricted to metals. The E series is electrically conductive and provides inherent EMI/RFI shielding characteristics. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.56 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D551 | ||
| Flow | 0.45 | % | |
| Across Flow | 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10600 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 50.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 0.60 | % | ISO 527-2 |
| Flexural Modulus | 10000 | MPa | ISO 178 |
| Flexural Stress | 70.0 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Heat | 1100 | J/kg/°C | ASTM E1461 |
| Thermal Conductivity | 20 | W/m/K | ASTM E1461 |
| Thermal Diffusivity | 0.100 | cm²/s | ASTM E1461 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.00 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 | °C | |
| Drying Time | 12 to 24 | hr | |
| Dew Point | -40.0 | °C | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 221 to 252 | °C | |
| Middle Temperature | 232 to 277 | °C | |
| Front Temperature | 238 to 277 | °C | |
| Nozzle Temperature | 238 to 277 | °C | |
| Processing (Melt) Temp | 232 to 282 | °C | |
| Mold Temperature | 38.0 to 93.0 | °C | |
| Injection Pressure | 5.20 to 13.8 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 3.40 to 10.3 | MPa | |
| Back Pressure | 0.500 to 3.00 | MPa | |
| Screw Speed | 50 to 150 | rpm | |
| Cushion | 6.30 to 12.7 | mm | |
| Screw Compression Ratio | 2.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD A 1480 | RTP Company | PESU | RTP |
| SEETEC LLDPE U8835 | Lotte Chemical Corporation | LLDPE | SEETEC LLDPE |
| Nypol® PA B3 HL VRD0246 NT342 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| Badaflex® TPE-S 50D 1000 | Bada AG | TPE | Badaflex® |
| Hanwha Total PP TB52M | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |