Retpol® 7250 UV2
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Retpol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xk5nfW_Retpol-7250-UV2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Propak 7250 UV2 is a 20% talc filled homopolymer polypropylene compound. It is a low flow injection moulding grade developed for rigid components and is manufactured in accordance with Australian Standard AS 2070, "Plastic Materials for Food Contact Use", and the ingredients used in this formulation are referenced in the US Code of Federal Regulations, Volume 21. It has been stabilized to withstand intermittent exposure to UV radiation. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 1.0 to 1.4 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.00 mm) | 100 | ASTM D785 | |
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 3.00 mm | 77 | ||
| Shore D, 15 sec, 3.00 mm | 72 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.00 mm) | 31.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.00 mm) | 50 | % | ASTM D638 |
| Flexural Modulus (3.00 mm) | 2380 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.00 mm) | 28 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.00 mm) | 440 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.00 mm | 128 | °C | |
| 1.8 MPa, Unannealed, 3.00 mm | 67.0 | °C | |
| CLTE - Flow (-30 to 30°C, 3.00 mm) | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 200 to 260 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP HDPE | Quadrant Engineering Plastic Products | HDPE | Quadrant EPP |
| Monprene® CP-10180 X (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |
| Axiall PVC 10705 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| OP - Acetal C-Acetal 10MF | Oxford Polymers | Acetal (POM) Copolymer | OP - Acetal |
| NORDEL™ IP 3760P | The Dow Chemical Company | EPDM | NORDEL™ |