Starex LX-9140
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xiQvI5_StarexLX9140.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starex LX-9140 is an acrylonitrile-styrene-acrylate (ASA) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Starex LX-9140 applications include electrical/electronic applications and electrical appliances. The main characteristics are: good weather resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.06 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 3.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.44 - 0.53 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.46 - 0.57 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.46 - 0.57 | % | ISO 2577 |
| Traffic : 3.20mm | 0.44 - 0.53 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 96 | ASTM D785 | |
| R scale | 96 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1900 | MPa | ASTM D638 |
| -- | 2000 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 42.0 | MPa | ASTM D638 |
| Yield | 45.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 44.0 | MPa | ASTM D638 |
| Fracture | 34.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture 4 | 110 | % | ASTM D638 |
| Fracture | 18 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 1900 | MPa | ASTM D790 |
| -- 6 | 2000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 57.0 | MPa | ASTM D790 |
| -- 8 | 66.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 9.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 98 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 59 | J/m | ASTM D256 |
| 23°C 10 | 6.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 96.0 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 4.00mm | 91.0 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 84.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 77.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 95.0 | °C | ISO 306/B50 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx CPP5B10 | The Matrixx Group, Inc. | PP Copolymer | Matrixx |
| TRIREX® 3020U(02) | Samyang Corporation | PC | TRIREX® |
| UBESTA 3024 LU | UBE Engineering Plastics, S.A. | Nylon 12 | UBESTA |
| Nypol® PA A3 T40 VRD0240 NR373 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Karina WHITE PVC COMPOUND 802-10/55-AY-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |