Plaslube® PA4/6 CF30 TL10
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Plaslube® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xhiwph_Plaslube-PA4-6-CF30-TL10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Plaslube® PA4/6 CF30 TL10 is a Polyamide 46 (Nylon 46) product filled with 30% carbon fiber. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.18 mm | 0.10 to 0.30 | % | |
| Across Flow : 3.18 mm | 0.40 to 0.70 | % | |
| Water Absorption (24 hr) | 2.0 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 193 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.6 | % | ASTM D638 |
| Flexural Modulus | 17900 | MPa | ASTM D790 |
| Flexural Strength | 290 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Steel - Dynamic | 0.15 | ||
| vs. Steel - Static | 0.16 | ||
| Wear Factor | 30 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 75 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 293 | °C | |
| 1.8 MPa, Unannealed | 285 | °C | |
| Melting Temperature | 295 | °C | |
| CLTE - Flow | 2.7E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 10 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| TPCI # | 8661150 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 282 to 316 | °C | |
| Middle Temperature | 282 to 316 | °C | |
| Front Temperature | 282 to 316 | °C | |
| Processing (Melt) Temp | 246 to 316 | °C | |
| Mold Temperature | 87.8 to 127 | °C | |
| Back Pressure | 0.00 to 0.345 | MPa | |
| Screw Speed | 40 to 80 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E198 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Tarnoform® 300 GF6 | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| DOMAMID® 66G25V0P 1003 A | DOMO Engineering Plastics SPA | Nylon 66 | DOMAMID® |
| Gallonprene® GP410-8003 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| apigo bio® CM 800 | API SpA | TPO (POE) | apigo bio® |