RTP 205 FR MS
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xgin1f_RTP-205-FR-MS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.- |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.76 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.60 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 13100 | MPa | ASTM D638 |
| Tensile Strength | 152 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.1 | % | ASTM D638 |
| Flexural Modulus | 10300 | MPa | ASTM D790 |
| Flexural Strength | 231 | MPa | ASTM D790 |
| Compressive Strength | 121 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 80 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 690 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 249 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 232 | °C | ASTM D648 |
| CLTE - Flow | 3.4E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.33 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 19 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 4.40 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.015 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 4mil/in. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 246 - 274 | °C | |
| Middle Temperature | 246 - 274 | °C | |
| Front Temperature | 246 - 274 | °C | |
| Mold Temperature | 65.6 - 107 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® LQ3187 | Covestro - Polycarbonates | PC | Makrolon® |
| Durethan® C 38 FA 000000 | LANXESS Asia/Pacific | Nylon 6 | Durethan® |
| KEBATRON® PPS L2040G3 | BARLOG plastics GmbH | PPS | KEBATRON® |
| 3M™ Dyneon™ PTFE Compound TF R4215 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| Sylvin 8950-55FU Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |