CONTINUUM™ DGDA-2492N NT
| Category: | HDPE , Bimodal Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | CONTINUUM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xgCd67_CONTINUUM-DGDA-2492N-NT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CONTINUUM™ DGDA-2492N NT Bimodal Polyethylene Resin is produced using UNIPOL™ II process technology. This product may be utilized for pipe applications where long-term hydrostatic strength combined with outstanding resistance to slow crack growth, rapid crack propagation, and high melt strength is desired. Suitable applications include water pipes at nuclear power facilities, natural gas distribution pipes, large diameter industrial piping, mining, sewage, and municipal water service lines. Industrial Standards Compliance: ASTM D 3350: cell classification
NOTES: Natural resin extruded under proper conditions with carbon black masterbatch DFNF-0092 (6.5%). |
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | ASTM D1505 | ||
| -- 1 | 0.949 | g/cm³ | ASTM D1505 |
| -- 2 | 0.959 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.060 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 5.5 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 3(Yield) | 24.8 | MPa | ASTM D638 |
| Tensile Elongation 4(Break) | 740 | % | ASTM D638 |
| Flexural Modulus | 1030 | MPa | ASTM D790B |
| Resistance to rapid crack propagation, Pc | |||
| Full Scale : 0°C 5 | > 45.9 | bar | ISO 13478 |
| S-4 : 0°C 6 | > 12.0 | bar | ISO 13477 |
| resistant to rapid crack propagation, Tc- S-4 7 | °C | ISO 13477 | |
| Slow crack propagation PENT 8 | > 10000 | hr | ASTM F1473 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermal Stability | > 220 | °C | ASTM D3350 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 9(23°C) | 490 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature 10 | < -75.0 | °C | ASTM D746A |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 193 - 227 | °C |
| Extrusion instructions |
|---|
| 制造条件： 螺杆类型：高质量 HDPE（对于完全熔解最好使用阻隔） 熔体温度范围：380-440°F (193-225°C) |
| Note Message | |
|---|---|
| 1 . | Natural resin |
| 2 . | Black compound |
| 3 . | Prepare compression molded fittings according to ASTM D 4703 procedure C, unless otherwise specified in the test method. Attributes will vary with molding conditions and aging time. |
| 4 . | Prepare compression molded fittings according to ASTM D 4703 procedure C, unless otherwise specified in the test method. Attributes will vary with molding conditions and aging time. |
| 5 . | Calculated value, determined by the equation in ISO 4437 based on S-4 test data. Pipe diameter of 10 inch IPS (25.4 cm) and Standard Diameter Ratio (SDR) 11. |
| 6 . | The pipe diameter is 10 inches IPS (25.4cm) and the standard diameter ratio (SDR) is 11. |
| 7 . | The pipe diameter is 10 inches IPS (25.4cm) and the standard diameter ratio (SDR) is 11. |
| 8 . | Prepare compression molded fittings according to ASTM D 4703 procedure C, unless otherwise specified in the test method. Attributes will vary with molding conditions and aging time. |
| 9 . | Prepare compression molded fittings according to ASTM D 4703 procedure C, unless otherwise specified in the test method. Attributes will vary with molding conditions and aging time. |
| 10 . | Prepare compression molded fittings according to ASTM D 4703 procedure C, unless otherwise specified in the test method. Attributes will vary with molding conditions and aging time. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 6193-89 Natural | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| apifive® DP1171/1/270 | API SpA | Polyolefin, Unspecified | apifive® |
| Avantra® 8930 | PMC Group Polymer Products | PS (HIPS) | Avantra® |
| Expandable PS RF23W-n | INEOS Styrenics International SA | PS (EPS) | Expandable PS |
| Elastron® D D400.D62.B | Elastron USA, Inc. | SBS | Elastron® D |