Petrothene® L2560S
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Petrothene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xg9Qip_Petrothene-L2560S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PETROTHENE L 2560S is a fractional melt index LDPE resin that exhibits a good balance of strength, clarity and heat seal characteristics. L 2560S is formulated without slip but with a medium antiblock level. Typical applications include produce bags, shrink wrap, frozen food containers, bundling and diaper films. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.925 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.60 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 32 µm, blown film | 248 | MPa | ASTM D882 |
| 1% secant, MD : 51 µm, blown film | 228 | MPa | ASTM D882 |
| 1% secant, TD : 32 µm, blown film | 290 | MPa | ASTM D882 |
| 1% secant, TD : 51 µm, blown film | 269 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 32 µm, blown film | 11.0 | MPa | ASTM D882 |
| MD : Yield, 51 µm, blown film | 11.0 | MPa | ASTM D882 |
| TD : Yield, 32 µm, blown film | 11.7 | MPa | ASTM D882 |
| TD : Yield, 51 µm, blown film | 11.7 | MPa | ASTM D882 |
| MD : Broken, 32 µm, blown film | 24.1 | MPa | ASTM D882 |
| MD : Broken, 51 µm, blown film | 20.0 | MPa | ASTM D882 |
| TD : Broken, 32 µm, blown film | 17.2 | MPa | ASTM D882 |
| TD : Broken, 51 µm, blown film | 17.2 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 32 µm, blown film | 120 | % | ASTM D882 |
| MD : Broken, 51 µm, blown film | 230 | % | ASTM D882 |
| TD : Broken, 32 µm, blown film | 500 | % | ASTM D882 |
| TD : Broken, 51 µm, blown film | 540 | % | ASTM D882 |
| Dart Drop Impact | ASTM D1709 | ||
| 32 µm, blown film | 80 | g | ASTM D1709 |
| 51 µm, blown film | 120 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 32 µm, blown film | 150 | g | ASTM D1922 |
| MD : 51 µm, blown film | 450 | g | ASTM D1922 |
| TD : 32 µm, blown film | 150 | g | ASTM D1922 |
| TD : 51 µm, blown film | 300 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 45 °, 31.8 µm, blown film | 60 | ASTM D2457 | |
| 45, 50.8 µm, blown film | 67 | ASTM D2457 | |
| Haze | ASTM D1003 | ||
| 31.8 µm, blown film | 8.5 | % | ASTM D1003 |
| 50.8 µm, blown film | 8.5 | % | ASTM D1003 |
| Additional Information |
|---|
| Data obtained from films produced in a 2" commercially available extruder with a 4" die, 309°F Melt Temperature, 2:1 BUR, 0.025" die gap at 50 lb/hr. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 885 | RTP Company | Acetal (POM) Copolymer | RTP |
| Novalloy-C CB4830 | Daicel Polymer Ltd. | PC+Polyester | Novalloy-C |
| BMC 840 | Bulk Molding Compounds, Inc. | Vinyl Ester | BMC |
| Globalene® SJ3032 | Lee Chang Yung Chemical Industry Corp. | PP Alloy | Globalene® |
| PENTAMID A GK30 H LS natural | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |