SABIC® FORTIFY™ C1085
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® FORTIFY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xfZvVp_SABICFORTIFYC1085.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® FORTIFY™ C1085 is an ethylene octene copolymer produced by solution polymerization using metallocene catalyst. This product is available as free flowing pellets. SABIC® FORTIFY™ C1085 is designed as a low density and high performance copolymer modifier to provide superior impact properties and flow characteristics. Typical application is wire and cable extrusion. Please take notice of specific storage and handling conditions. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.885 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Mooney Viscosity (ML 1+4, 121°C) | 21 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A, 1 sec | 81 | ASTM D2240 | |
| Shaw D, 1 sec | 29 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 100% Secant | 4.60 | MPa | ASTM D638 |
| Tensile Strength (Break) | 16.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 700 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | 29.4 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 1 | 58.8 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -47.0 | °C | Internal method |
| Melting Temperature | 74.0 | °C | Internal method |
| Additional Information |
|---|
| All physical properties were measured on compression molded specimens. |
| Note Message | |
|---|---|
| 1 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefabloc® TP SD 310 50A | Mitsubishi Chemical Performance Polymers, Inc. | TPE | tefabloc® |
| Skyrol® SH94 | SKC Inc. | PET | Skyrol® |
| Delta ATL C27 | Delta Polymers | Acetal (POM) Copolymer | Delta |
| LNP™ LUBRICOMP™ RL002 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |
| Sylvin 9604-85C Grey 935 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |