HiFill® PEI GF10
| Category: | PEI , Polyether Imide |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xergwr_HiFill-PEI-GF10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HiFill® PEI GF10 is a Polyether Imide (PEI) product filled with 10% glass fiber. It can be processed by injection molding and is available in North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.22 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 121 | MPa | ASTM D638 |
| Flexural Modulus | 5170 | MPa | ASTM D790 |
| Flexural Strength | 203 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 210 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 141 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 357 to 391 | °C | |
| Middle Temperature | 357 to 391 | °C | |
| Front Temperature | 357 to 391 | °C | |
| Processing (Melt) Temp | 354 to 388 | °C | |
| Mold Temperature | 135 to 163 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Karina STRAW COLOR CONCENTRATE 38/ 98-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Hostacom PPU X9067HS D82513 | LyondellBasell Industries | PP Copolymer | Hostacom |
| SD POLYCA™ SI6001W | Sumika Styron Polycarbonate Limited | PC | SD POLYCA™ |
| Tritan™ LX100 | Eastman Chemical Company | Copolyester | Tritan™ |
| Styropek® BFL 495 | Styropek S.A. de C.V. | PS (EPS) | Styropek® |