Hytrel® HTR8206
| Category: | TPC-ET , THERMOPLASTIC POLYESTER ELASTOMER |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Hytrel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xeQ380_HytrelHTR8206.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High Performance Polyester Elastomer with High Moisture Vapor Transmission Rate Developed for Extrusion and Injection Molding |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/2.16 kg) | 14.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 1.5 | % | ISO 294-4 |
| Flow | 1.4 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 35 | % | ISO 62 |
| Balance, 23°C, 2.00mm, 50% RH | 1.3 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ISO 868 | ||
| Shaw D | 40 | ISO 868 | |
| Shaw D, 15 seconds | 38 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 80.0 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Fracture | 20.0 | MPa | ISO 527-2 |
| 5.0% strain | 3.40 | MPa | ISO 527-2 |
| 10% strain | 5.40 | MPa | ISO 527-2 |
| 50% strain | 9.50 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 300 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 420 | % | ISO 527-2 |
| Flexural Modulus | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | No Break | ISO 179/1eA | |
| 23°C | No Break | ISO 179/1eA | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature 1 | 200 | °C | ISO 11357-3 |
| Effective Thermal Diffusivity 2 | 5.44E-8 | m²/s |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| FMVSS Flammability | B | FMVSS 302 |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Specific Heat Capacity of Melt 3 | 2100 | J/kg/°C | |
| Thermal Conductivity of Melt 4 | 0.16 | W/m/K |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature, Optimum | 230 | °C | |
| Mold Temperature, Optimum | 45 | °C | |
| Drying Recommended | yes |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 5(1.00 mm) | < 100 | mm/min | ISO 3795 |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Melt Density | 1.02 | g/cm³ |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time - Desiccant Dryer | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.080 | % | |
| Processing (Melt) Temp | 220 - 240 | °C | |
| Mold Temperature | 40 - 50 | °C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | Derived from Similar Grade |
| 3 . | Derived from Similar Grade |
| 4 . | Derived from Similar Grade |
| 5 . | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SHIN-A SE-5015P | SHIN-A T&C | Epoxy | SHIN-A |
| NEXUS BIO BIO-200 | Nexus Resin Group, LLC. | Biodeg Polymers | NEXUS BIO |
| LNP™ LUBRICOMP™ AL003 compound | SABIC Innovative Plastics | ABS | LNP™ LUBRICOMP™ |
| Sylvin 8225-95UV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| SIBUR Synthetic Rubber NBR 4055 | SIBUR | NBR | SIBUR Synthetic Rubber |