ULTEM™ 6202 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xeGDpo_ULTEM6202resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 12% Silica filled, standard flow Polyetherimide Copolymer (Tg 235C). ECO Conforming, UL94 VO Listing. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (360°C/5.0 kg) | 8.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.50 - 0.70 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 160 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3700 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 90.0 | MPa | ISO 527-2/5 |
| Fracture | 90.0 | MPa | ISO 527-2/5 |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 5.0 | % | ISO 527-2/5 |
| Fracture | 7.0 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 3800 | MPa | ISO 178 |
| Flexural Stress | 150 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 35.0 | mg | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength 3 | ISO 179/1eU | ||
| -30°C | 25 | kJ/m² | ISO 179/1eU |
| 23°C | 50 | kJ/m² | ISO 179/1eU |
| Unnotched Izod Impact Strength 4 | ISO 180/1U | ||
| -30°C | 45 | kJ/m² | ISO 180/1U |
| 23°C | 40 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, unannealed, 100 mm span | 215 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 202 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 222 | °C | ISO 306/B50 |
| -- | 225 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 80°C | 4.5E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 23 to 150°C | 4.5E-5 | cm/cm/°C | ISO 11359-2 |
| Horizontal : 23 to 150°C | 4.5E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.28 | W/m/K | ISO 8302 |
| RTI Elec | 105 | °C | UL 746 |
| RTI Imp | 105 | °C | UL 746 |
| RTI | 105 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | IEC 60243-1 | ||
| 1.60mm, in oil | 21 | kV/mm | IEC 60243-1 |
| 3.20mm, in oil | 17 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 2.90 | IEC 60250 | |
| 60 Hz | 2.90 | IEC 60250 | |
| 1 MHz | 2.80 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 4.0E-3 | IEC 60250 | |
| 60 Hz | 4.0E-3 | IEC 60250 | |
| 1 MHz | 3.0E-3 | IEC 60250 | |
| Comparative Tracking Index | 150 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 | |
| Oxygen Index | 48 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 |
| 5 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E885 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| THERMOLAST® K TF6PEN (Series: FC/AD/PE) | KRAIBURG TPE | TPE | THERMOLAST® K |
| TRIMMA® SD6310H | Samyang Corporation | Acrylic (PMMA) | TRIMMA® |
| FLEXAREN® 18002 | Innospec Leuna GmbH | EVA | FLEXAREN® |
| LEXAN™ 123X resin | SABIC Innovative Plastics | PC | LEXAN™ |