REVOLVE® N-265
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | Matrix Polymers |
| Trademark: | REVOLVE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xeCRPu_REVOLVE-N-265.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Revolve N-265 is a fully formulated rotational moulding grade especially suitable for general purpose applications where extra impact strength is required. This grade is ideal for applications such as small tanks and other "industrial" items. This grade is also suitable for ESCR and chemical resistance applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.935 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 3.0 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance | ASTM D1693 | ||
| 10% Igepal | 600 | hr | |
| 100% Igepal | > 1000 | hr |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 15.7 | MPa | ISO 527-2/50 |
| Flexural Modulus 1 | 605 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Low Temperature Impact - ARM (3.00 mm) | 72.9 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 46.0 | °C | ISO 75-2/B |
| Note Message | |
|---|---|
| 1 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 600.5 | RTP Company | ABS | RTP |
| Axiall PVC 7456 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Aurora PVC AP1143 Series | Aurora Plastics, Inc. | PVC, Unspecified | Aurora PVC |
| Hostacom EKC 334N BLACK | LyondellBasell Industries | PP Copolymer | Hostacom |
| LNP™ KONDUIT™ OX10324 compound | SABIC Innovative Plastics Asia Pacific | PPS | LNP™ KONDUIT™ |