EPO-TEK® 301-2
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xe6sCR_EPO-TEK-301-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EPO-TEK® 301-2 is a two component optical, medical, and semiconductor grade epoxy resin, with low viscosity, long pot-life, and good handling characteristics. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Ion Type | |||
| Cl- | 61 | ppm | |
| K+ | Not Detectable | ||
| Na+ | 104 | ppm | |
| NH4+ | Not Detectable |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Degradation Temperature | 360 | °C | TGA |
| Die Shear Strength - >15 kg (23°C) | 35.2 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 200 | °C | |
| Intermittent | -55 to 300 | °C | |
| Storage Modulus | 2.06 | GPa | |
| Weight Loss on Heating | |||
| 200°C | 0.010 | % | |
| 250°C | 0.46 | % | |
| 300°C | 2.2 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | > 80.0 | °C | |
| CLTE - Flow | |||
| -- 2 | 6.1E-5 | cm/cm/°C | |
| -- 3 | 1.8E-4 | cm/cm/°C |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Refractive Index 4 | 1.532 | ||
| Transmittance | |||
| 320 nm | > 94.0 | % | |
| 400 to 1200 nm | > 99.0 | % | |
| 1200 to 1600 nm | > 98.0 | % |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100 | ||
| Part B | Mix Ratio by Weight: 35 | ||
| Shelf Life (23°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 5 | Clear/Transparent | ||
| -- 6 | Clear/Transparent | ||
| Density | |||
| Part B | 0.888 | g/cm³ | |
| Part A | 1.02 | g/cm³ | |
| Viscosity 7(23°C) | 0.23 to 0.43 | Pa·s | |
| Curing Time (80°C) | 3.0 | hr | |
| Pot Life | 480 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 80 | ||
| Lap Shear Strength (23°C) | > 13.8 | MPa | |
| Relative Permittivity (1 kHz) | 3.80 | ||
| Volume Resistivity | > 2.0E+12 | ohms·cm | |
| Dissipation Factor (1 kHz) | 0.012 |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | 589 nm |
| 5 . | Part B |
| 6 . | Part A |
| 7 . | 100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds HM-305W (Comp) | Ravago Manufacturing Americas, LLC | LMDPE | Ravago Compounds |
| NEXT REPROCESSED ABS LGA-300R | NEXT Specialty Resins, Inc. | ABS | NEXT REPROCESSED |
| EVALENE® PP PHF1001 | JG Summit Petrochemical Corporation | PP Homopolymer | EVALENE® PP |
| FRAGOM PR/720 | Crosspolimeri S.p.A. | Polyolefin, Unspecified | FRAGOM |
| EMAC® SP2260 | Westlake Chemical Corporation | EMA | EMAC® |