PRE-ELEC® PS 1340
| Category: | PS Alloy , Polystyrene Alloy |
| Manufacturer: | Premix Oy |
| Trademark: | PRE-ELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xdhlIv_PRE-ELEC-PS-1340.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRE-ELEC® PS 1340 is a conductive thermoplastic concentrate based on polystyrene. Conductivity is achieved by using a high concentration of special conductive carbon black. PRE-ELEC® PS 1340 can be diluted up to 60% with virgin or recycled polystyrene. The actual amount should always be tested as it also depends on the processing conditions. Typical applications include mono- or co-extruded sheets for thermoformed trays. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/21.6 kg) | 1.2 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.40 - 0.60 | % | ASTM D955 |
| Flow direction | 0.40 - 0.60 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ISO 868 | ||
| Shaw A | 98 | ISO 868 | |
| Shaw D | 73 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 33.8 | MPa | ASTM D638 |
| Yield | 34.0 | MPa | ISO 527-2 |
| -- | 40.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation | ASTM D638, ISO 527-2 | ||
| Yield | 4.0 | % | ASTM D638, ISO 527-2 |
| Fracture | 30 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 1900 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -20°C 1 | 6.3 | kJ/m² | ASTM D256 |
| -20°C 2 | 6.0 | kJ/m² | ISO 179 |
| 23°C 3 | 11 | kJ/m² | ISO 179, ASTM D256 |
| Charpy Unnotched Impact Strength 4 | |||
| -20°C | 61 | kJ/m² | ASTM D256 |
| -20°C | 60 | kJ/m² | ISO 179 |
| 23°C | No Break | ISO 179, ASTM D256 | |
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 4.00 mm | 4.20 | kJ/m² | ASTM D256 |
| 23°C, 4.00 mm | 52.5 | kJ/m² | ASTM D256 |
| Notched Izod Impact 5 | ISO 180 | ||
| -20°C | 5.0 | kJ/m² | ISO 180 |
| 23°C | 52 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | ASTM D256 | ||
| -20°C, 4.00 mm | 54.6 | kJ/m² | ASTM D256 |
| 23°C, 4.00 mm | No Break | ASTM D256 | |
| Unnotched Izod Impact Strength 6 | ISO 180 | ||
| -20°C | 55 | kJ/m² | ISO 180 |
| 23°C | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 75.0 | °C | ASTM D648B, ISO 75-2/Bf |
| 1.8 MPa, not annealed | 66.1 | °C | ASTM D648A |
| 1.8 MPa, not annealed | 66.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 83.9 | °C | ASTM D1525 7 |
| -- | 102 | °C | ASTM D1525, ISO 306/A50 5 8 |
| -- | 84.0 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+5 | ohms | ESD STM11.11, IEC 61340-2-3 |
| Volume Resistivity | < 1.0E+4 | ohms·cm | Internal method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 80.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 180 | °C | |
| Cylinder Zone 2 Temp. | 200 | °C | |
| Cylinder Zone 3 Temp. | 200 | °C | |
| Cylinder Zone 4 Temp. | 210 | °C | |
| Cylinder Zone 5 Temp. | 210 | °C |
| Extrusion instructions |
|---|
| Cylinder Zone 6: 210°C |
| Note Message | |
|---|---|
| 1 . | 4 mm thickness |
| 2 . | 4 mm thick |
| 3 . | 4 mm thick |
| 4 . | 4 mm thick |
| 5 . | 4 mm thick |
| 6 . | 4 mm thick |
| 7 . | 标准 B (120°C/h), 载荷2 (50N) |
| 8 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PP GP3201 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| EverGlide® MB1950WC | Polymer Dynamix | Nylon 6 | EverGlide® |
| Fiberfil® M-2500 BK | Fiberfil® Engineered Plastics Inc. | Nylon 6 | Fiberfil® |
| Leona™ 91G55 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| Aquivion® D79-25BS-Li | Solvay Specialty Polymers | PFSA Lithium Salt | Aquivion® |