T & T Marketing TPE 5280
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | T & T Marketing, Inc. |
| Trademark: | T & T Marketing |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xdTFlw_T-T-Marketing-TPE-5280.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TPE 5280 is a natural, olefin-based thermoplastic elastomer (TPE) intended for flexible cable, welding cable and general purpose cable jacketing. This dynamically crosslinked compound offers a low-modulus and excellent low temperature flexibility. TPE 5280 exhibits good extrusion processing characteristics on either conventional polyethylene or PVC extrusion lines. TPE 5280 is readily pigmented to a variety of colors using standard wire and cable color concentrates designed for thermoplastic or crosslinked polyolefins. UV weather resistance is obtainable by the addition of a suitable carbon black or UV additive. Application TPE 5280 is intended for low voltage flexible cable and welding cable jacketing usage. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.890 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A, 0.762mm | 80 | ASTM D2240 | |
| Shore D, 0.762mm | 35 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (0.762 mm) | 15.2 | MPa | ASTM D412 |
| Tensile Elongation (Break, 0.762 mm) | 600 | % | ASTM D412 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile strength retention- 7 days at 136°C (762.0 µm) | > 95 | % | UL 1581 |
| Elongation retention rate- 7 days at 136°C (762.0 µm) | > 95 | % | UL 1581 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deformation (150°C, 762.0 µm) | % | UL 1581 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Extruder Screw L/D Ratio | 24:1 | ||
| Extruder Screw Compression Ratio | 2.7 to 3.5:1 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -45.6 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1(1.91 mm) | 26 | kV/mm | ASTM D149 |
| Dielectric Constant (1.91 mm, 60 Hz) | 2.20 | ASTM D150 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 188 | °C | |
| Cylinder Zone 2 Temp. | 199 | °C | |
| Cylinder Zone 3 Temp. | 204 | °C | |
| Cylinder Zone 4 Temp. | 210 | °C | |
| Melt Temperature | 210 | °C | |
| Die Temperature | 210 - 232 | °C |
| Extrusion instructions |
|---|
| Screw: Barrier or Single FlightDie: Smooth transition, With >= 1/8 in. land, Die & Tip include angle: 22-35°Throat: Water-cooled |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCANAMID 6 B12^ F50 | Polykemi AB | Nylon 6 | SCANAMID 6 |
| Nypol® PA B3 HF CNZA011 NT384 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| Crystal Clear® 202 | Smooth-On, Inc | PUR, Unspecified | Crystal Clear® |
| Ecotan A FL HI 2 NERO | Soredi S.p.a. | Nylon 66 | Ecotan A |
| Generic PBT - Proprietary | Generic | PBT | Generic |