SPI 962 BK
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Service Polymers, Inc. |
| Trademark: | SPI |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xdPBXK_SPI-962-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SPI 962 BK is a Polyamide 66 (Nylon 66) product filled with 40% carbon fiber. It is available in North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.10 to 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 26500 to 28600 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 193 to 218 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 1.0 to 3.0 | % | ASTM D638 |
| Flexural Modulus | 22400 to 24500 | MPa | ASTM D790 |
| Flexural Strength | 362 to 379 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 75 to 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 250 to 253 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 4.0 | hr | |
| Dew Point | -17.8 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 277 to 299 | °C | |
| Mold Temperature | 65.6 to 107 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vexel PBT B50GF30 | Custom Resins Group | PBT | Vexel |
| Jiangsu Sinarise JM8513 | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |
| Karina BLACK PVC COMPOUND TR-751D48/ 1-E-IS (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Ducor® 1105 N | Ducor Petrochemicals BV | PP Homopolymer | Ducor® |
| LEXAN™ HFD1212 resin | SABIC Innovative Plastics | PC | LEXAN™ |