Cevian®-V SERG1
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Daicel Polymer Ltd. |
| Trademark: | Cevian®-V |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xdCMVk_Cevian--V-SERG1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Cevian®-V SERG1 is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific. Primary attribute of Cevian®-V SERG1: Flame Rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.20 to 0.50 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 114 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 75.0 | MPa | ISO 527-2 |
| Flexural Modulus | 4700 | MPa | ISO 178 |
| Flexural Stress | 110 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 5.0 | kJ/m² | |
| 23°C | 8.0 | kJ/m² | |
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 6.40 mm | 40 | J/m | |
| 23°C, 6.40 mm | 80 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 12.7 mm | 94.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 86.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 91.0 | °C | ISO 306/B50 |
| CLTE | ISO 11359-2 | ||
| Flow | 5.0E-5 | cm/cm/°C | |
| Transverse | 8.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (1.50 mm) | 34 | kV/mm | ASTM D149 |
| Arc Resistance (3.00 mm) | 10.0 | sec | ASTM D495 |
| Arc Resistance (3.00 mm) | PLC 7 | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.70 mm | V-0 | ||
| 2.50 mm | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 160 to 180 | °C | |
| Middle Temperature | 180 to 200 | °C | |
| Front Temperature | 200 to 220 | °C | |
| Nozzle Temperature | 200 to 220 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Back Pressure | 10.0 to 20.0 | MPa | |
| Screw Speed | 40 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M8180 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Manner Flexible PVC V941 BLK 580 AF | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| FHR EPS 40-6340 | Flint Hills Resources, LP | PS (EPS) | FHR EPS |
| FR-PET® B3045FA | Polyplastics Co., Ltd. | PET | FR-PET® |
| Paracril® P7092P | INSA | NBR | Paracril® |