Lumiloy® GN4356F
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lumiloy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xcqlyP_Lumiloy-GN4356F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Injection Molding Grade, Flame Retardent mPPO Description High Strength & Modulus, GF & Mineral 35% Reinforced, High Flow Application Electric and Electronic Parts |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 280°C/5.0 kg | 19 | g/10 min | |
| 300°C/5.0 kg | 46 | g/10 min |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield, 3.20 mm | 108 | MPa | |
| Break, 3.20 mm | 108 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield, 3.20 mm | 6.0 | % | |
| Break, 3.20 mm | 6.0 | % | |
| Flexural Modulus 3(3.20 mm) | 8730 | MPa | ASTM D790 |
| Flexural Strength 4(Break, 3.20 mm) | 157 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 69 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C, 3.20 mm) | 350 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 121 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-1 | ||
| 3.20 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Suggested Max Moisture | > 0.030 | % | |
| Rear Temperature | 270 to 310 | °C | |
| Middle Temperature | 280 to 310 | °C | |
| Front Temperature | 280 to 310 | °C | |
| Nozzle Temperature | 270 to 310 | °C | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 80.0 to 110 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unigel PS U8878 | Unigel Plásticos | PS (HIPS) | Unigel PS |
| NEXT REGRIND PA6 8267-300RG | NEXT Specialty Resins, Inc. | Nylon 6 | NEXT REGRIND |
| Formolene® 5143S | Formosa Plastics Corporation, U.S.A. | PP Homopolymer | Formolene® |
| POLYCOMPO PE 2200J | POLYCOMPO Co.,Ltd. | HDPE | POLYCOMPO PE |
| Optix® CA-8115 | Plaskolite, Inc. | Acrylic (PMMA) | Optix® |