3M™ Dyneon™ Fluoroelastomer FE 5625N

Category:	Fluorelastomer , Fluoroelastomer
Manufacturer:	3M Advanced Materials Division
Trademark:	3M™ Dyneon™ Fluoroelastomer
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	xcVKFA_3MDyneonFluoroelastomerFE5625N.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
3M™ Dyneon™ Fluoroelastomer FE 5625N is a dipolymer made from hexafluoropropylene and vinylidene fluoride. FE 5625N has an incorporated bisphenol cure system. Special Features Composition: dipolymer of vinylidene fluoride and hexafluoropropylene Process targets: injection and transfer moulding, extrusion and calendering Proprietary incorporated cure technology Cure profile adjusted for use in automatic multi cavity moulding equipment Superior flow over regular 3M™ Dyneon™ Fluoroelastomer injection moulding grades Improved scorch resistance at high moulding temperatures Excellent mould release - can be used in automated injection moulding equipment Clean running Typical Applications 3M™ Dyneon™ Fluoroelastomer FE 5625N is suitable for the production of O-rings in an injection moulding process.

Message

3M™ Dyneon™ Fluoroelastomer FE 5625N is a dipolymer made from hexafluoropropylene and vinylidene fluoride. FE 5625N has an incorporated bisphenol cure system.

Special Features

Composition: dipolymer of vinylidene fluoride and hexafluoropropylene

Process targets: injection and transfer moulding, extrusion and calendering

Proprietary incorporated cure technology

Cure profile adjusted for use in automatic multi cavity moulding equipment

Superior flow over regular 3M™ Dyneon™ Fluoroelastomer injection moulding grades

Improved scorch resistance at high moulding temperatures

Excellent mould release - can be used in automated injection moulding equipment

Clean running

Typical Applications
3M™ Dyneon™ Fluoroelastomer FE 5625N is suitable for the production of O-rings in an injection moulding process.

General Information
Features	Good demoulding performance
Uses	O-rings
Appearance	Opacity White-like
Forms	Thick sheet
Processing Method	Extrusion Resin transfer molding Calendering Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.80	g/cm³	Internal method
Mooney Viscosity (ML 1+10, 121°C)	20	MU	Internal method
Fluorine Content	66	%	Internal method

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	78		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress ¹(100% Strain)	6.80	MPa	ASTM D412A
Tensile Strength ²	13.0	MPa	ASTM D412A
Tensile Elongation ³(Break)	180	%	ASTM D412A
Compression Set			ASTM D1414
200°C, 70 hr ⁴	16	%	ASTM D1414
200°C, 70 hr ⁵	15	%	ASTM D1414

Note Message
1 .	D mould
2 .	Die D
3 .	D mould
4 .	Post cured 16 hours @ 230°C
5 .	Post cured 24 hours @ 260°C

Resin Grade	Manufacturer	Category	Trademark
Topolymer® 9210-751	Dongguan Top Polymer Enterprise	TPV	Topolymer®
Desmopan® DP 3360A	Covestro - PUR	TPU-Polyester	Desmopan®
Evermore PUR UAP-9060	Evermore Chemical Industry Co., Ltd.	Acrylic, Unspecified	Evermore PUR
Haysite SMC 54500	Haysite Reinforced Plastics	Polyester, TS	Haysite SMC
Shida 2513	JINJIANG City SHIDA Plastic Fine Co., Ltd.	TPE	Shida