SLOVALEN® PQ 81 T 10
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Plastcom |
| Trademark: | SLOVALEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xbg6PD_SLOVALEN-PQ-81-T-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Modified PP for injection moulding with the content of 10% mineral filling. Increased rigidity, strength and thermal use up to 130°C depending on the talc content. Decreased shrinkage. General application in all industry branches - packing material, garden flower-pots, toys, furniture industry, dowels, clamps, hinge, office chairs, hangers, covers of car chassis, fenders, motors etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.940 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| Molding Shrinkage | STM 64 0808 | ||
| Across Flow | 1.2 | % | |
| Flow | 1.2 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1200 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 15.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 9.0 | % | ISO 527-2 |
| Flexural Modulus | 950 | MPa | ISO 178 |
| Flexural Stress | 18.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 5.0 | kJ/m² | |
| 23°C | 43 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 72.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 130 | °C | ISO 306/B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 200 to 250 | °C | |
| Mold Temperature | 40.0 to 50.0 | °C | |
| Injection Pressure | 70.0 to 120 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MBA PS 3122 70/42 | MBA Polymers | PS (GPPS) | MBA PS |
| S&E PVC G-3570 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E PVC |
| RheTech Polypropylene CC20P200-00 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Nypol® PA B3 G50 HS UV PRTA010 NT304 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| Karina BLACK PVC COMPOUND 600D48/1-A-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |