LNP™ STAT-KON™ TD000 compound
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xbdQsF_LNP-STAT-KON-TD000-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON TD000 is an unfilled compound based on Polyurethane resin. Added feature of this material is: Electrically Conductive. Also known as: LNP* STAT-KON* Compound T Product reorder name: TD000 |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 1.0 to 3.0 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.50 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.79 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 185 | MPa | ASTM D638 |
| -- | 305 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 26.0 | MPa | ASTM D638 |
| Yield | 24.0 | MPa | ISO 527-2/5 |
| Break | 25.5 | MPa | ASTM D638 |
| Break | 24.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 3 | 160 | % | ASTM D638 |
| Yield | 140 | % | ISO 527-2/5 |
| Break | 160 | % | ASTM D638 |
| Break | 140 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| -- | 368 | MPa | ASTM D790 |
| -- 4 | 354 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 6.89 | MPa | ASTM D790 |
| -- | 16.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 790 | J/m | ASTM D256 |
| 23°C 5 | 79 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1000 | J/m | ASTM D4812 |
| 23°C 6 | 87 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 50.7 | J | ASTM D3763 |
| -- | 55.5 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 70.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 7 | 69.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 47.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 8 | 48.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 1.2E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 1.4E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 3.0 to 5.0 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.0 to 104 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 193 to 210 | °C | |
| Middle Temperature | 193 to 216 | °C | |
| Front Temperature | 199 to 221 | °C | |
| Nozzle Temperature | 204 to 227 | °C | |
| Processing (Melt) Temp | 210 | °C | |
| Mold Temperature | 16.0 to 43.0 | °C | |
| Back Pressure | 0.170 to 0.340 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 mm |
| 8 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYNIL® P50 FLBK | Nilit Plastics | Nylon 66 | POLYNIL® |
| Sumitomo Silicone SI 9550 | Sumitomo Bakelite North America, Inc. | Silicone | Sumitomo Silicone |
| HIDEN® A015E IS | YUHWA Korea Petrochemical Ind. Co., Ltd. | HDPE | HIDEN® |
| Epiall® 1960B-1 | Sumitomo Bakelite North America, Inc. | Epoxy | Epiall® |
| Perflex TPE GP-50NE | CP Chemie Resources (M) Sdn. Bhd. | SEBS | Perflex |