OP - Acetal H-Acetal 10MF
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | Oxford Polymers |
| Trademark: | OP - Acetal |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xbRsUg_OP---Acetal-H-Acetal-10MF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
OP - Acetal H-Acetal 10MF is an Acetal (POM) Homopolymer material. It is available in North America for injection molding. Important attributes of OP - Acetal H-Acetal 10MF are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 to 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 65.5 | MPa | |
| Break | 65.5 | MPa | |
| Tensile Elongation (Break) | 13 | % | ASTM D638 |
| Flexural Modulus | 3170 | MPa | ASTM D790 |
| Flexural Strength | 68.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (4°C) | 64 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 118 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 113 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.59 mm | HB | ||
| 3.18 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 177 to 199 | °C | |
| Middle Temperature | 182 to 204 | °C | |
| Front Temperature | 188 to 210 | °C | |
| Processing (Melt) Temp | 182 to 218 | °C | |
| Mold Temperature | 79.4 to 107 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP PA66 15 GF 25 M BLK | RTP Company | Nylon 66 | RTP |
| Badaflex® TPE-S 50D 1040 | Bada AG | SEBS | Badaflex® |
| BorSafe™ HE3496-LS | Borealis AG | HDPE | BorSafe™ |
| ESTOPLAST EP 5010NN12 | Ester Industries Ltd. | PBT | ESTOPLAST EP |
| POLYFLAM® RABS 90000 UV5 | A. Schulman Europe | ABS | POLYFLAM® |