SureSpec HP-080
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Genesis Polymers |
| Trademark: | SureSpec |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xaz7hn_SureSpec-HP-080.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HP-080 is a Polypropylene certified prime grade designed for Film EXTRUSON by Tubular Water Quench - TWQ - process. HP-080 combines excellent processability and good melt thermal stability, with films exhibiting clarity, good impact strength, modulus, good barrier to fats and oils, and good chemical resistance. HP-080 recommended processing temperature is between 210° to 230°C. HP-080 complies with FDA regulation 21CFR 177.1520 (a)(1) (b) (c)1.1, and most international regulations concerning Polypropylene use in contact with food articles. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.925 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus - 1% Secant 1 | 1380 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus 2 | ASTM D882 | ||
| 1% Secant, MD : 32 µm | 689 | MPa | |
| 1% Secant, TD : 32 µm | 689 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break | 55.2 | MPa | |
| TD : Break | 37.9 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break | 500 | % | |
| TD : Break | 550 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 32 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 102 | °C | ASTM D648 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss 3(45°, 31.8 µm, Blown Film) | 85 | ASTM D2457 | |
| Haze 4(31.8 µm, Blown Film) | 2.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 210 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | 1.3 mm/min |
| 2 . | 1.25 mils (31 µm) film, melt temperature 410-450°F (210-230°C), blow-up-ratio 1.5:1 |
| 3 . | 1.25 mils (31 µm) film, melt temperature 410-450°F (210-230°C), blow-up-ratio 1.5:1 |
| 4 . | 1.25 mils (31 µm) film, melt temperature 410-450°F (210-230°C), blow-up-ratio 1.5:1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCANBLEND SS7 | Polykemi AB | ASA+PC | SCANBLEND |
| Yuyao PPO N100A | Yuyao Tenglong Plastics Co., Ltd. | PPE+PS | Yuyao PPO |
| NEFTEKHIM PP 1500P (V30G) | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| Chemlon® 217 GI | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| Durepol® PBT A3 G30 CNZ0340 BT320 | Petropol Industry and Trade of Polymers LTDA | PBT | Durepol® PBT |