Cheng Yu T882GV1
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Cheng Yu Plastic Company Limited |
| Trademark: | Cheng Yu |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xaNufU_Cheng-Yu-T882GV1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Cheng Yu T882GV1 is a Polybutylene Terephthalate (PBT) product filled with 10% glass fiber. It is available in Asia Pacific. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.60 to 1.0 | % | |
| Across Flow | 1.3 to 1.6 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 94 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strength | 130 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 223 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Dielectric Constant (60 Hz) | 3.50 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ShinkoLite-P IR H-70 | Mitsubishi Rayon America Inc. | Acrylic (PMMA) | ShinkoLite-P |
| Niuk 20GP20 | Shanghai Niuk New Plastic Technology Co., Ltd. | ABS | Niuk |
| APEX® 582 | Teknor Apex Company | PVC, Flexible | APEX® |
| KEP® 110 | Kumho Polychem Co., Ltd. | EPM | KEP® |
| I. Stern PS2110 | I. STERN & CO. INC. | PS (GPPS) | I. Stern |