Badalac® ABS 20
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Bada AG |
| Trademark: | Badalac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xaD9RV_Badalac-ABS-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Easy flowing standard injection moulding grade for a wide range of applications, especially for housings |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.04 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 20.0 | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 1.0 | % | |
| Equilibrium, 23°C, 50% RH | 0.22 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C) | 2300 | MPa | ISO 527-2/1 |
| Tensile Stress 2(Yield, 23°C) | 45.0 | MPa | ISO 527-2/50 |
| Tensile Strain 3(Yield, 23°C) | 2.6 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break 4(23°C) | 10 | % | ISO 527-2/50 |
| Flexural Stress 5(23°C) | 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 6 | ISO 179/1eA | ||
| -30°C | 8.0 | kJ/m² | |
| 23°C | 22 | kJ/m² | |
| Charpy Unnotched Impact Strength 7 | ISO 179/1eU | ||
| -30°C | 100 | kJ/m² | |
| 23°C | 180 | kJ/m² | |
| Notched Izod Impact Strength 8 | |||
| -30°C | 8.0 | kJ/m² | ISO 180 |
| 23°C | 21 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 9 | |||
| 0.45 MPa, Unannealed | 103 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 99.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature 10 | |||
| -- | 105 | °C | ISO 306/A50 |
| -- | 96.0 | °C | ISO 306/B50 |
| CLTE - Flow 11 | 8.0E-5 to 1.1E-4 | cm/cm/°C | DIN 53752 |
| Maximum Service Temperature | IEC 216 | ||
| 20000 hrs | 80 | °C | |
| some hours | 0 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 12 | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity 13 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength 14 | 37 | kV/mm | IEC 60243-1 |
| Relative Permittivity 15(1 MHz) | 2.80 | IEC 60250 | |
| Dissipation Factor 16(1 MHz) | 7.9E-3 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 17(0.800 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 220 to 260 | °C | |
| Mold Temperature | 30.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | Test Specimen accordng to ISO 3167, Type A |
| 4 . | Test Specimen accordng to ISO 3167, Type A |
| 5 . | 80x10x4 mm |
| 6 . | 80x10x4 mm |
| 7 . | 80x10x4 mm |
| 8 . | 80x10x4 mm |
| 9 . | 110x10x4 mm |
| 10 . | Compound for moulding |
| 11 . | >=10x10x4 mm |
| 12 . | 80x80x1 mm |
| 13 . | 80x80x1 mm |
| 14 . | 80x80x1 mm |
| 15 . | 80x80x1 mm |
| 16 . | 80x80x1 mm |
| 17 . | 125x13x0.8 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Impax 250 | Primex Plastics Corporation | PS (HIPS) | Prime Impax |
| Sylvin 2910-55 Clear | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| ALCOM® POM 770/1 PTFE18 Si2 | ALBIS PLASTIC GmbH | Acetal (POM) Copolymer | ALCOM® POM |
| Fainplast PVC ART 0699 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Paracril® AJLT M60 | INSA | NBR | Paracril® |