Deltron 5311
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Shanghai Lin Gen Rubber Materials Co., Ltd. |
| Trademark: | Deltron |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xa0x3n_Deltron5311.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Deltron 5311 is a polyphenylene sulfide (PPS) material, which contains carbon fiber reinforcement. This product is available in the Asia-Pacific region and is processed by injection molding. The main characteristics of Deltron 5311 are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | 1.70 | g/cm³ | |
| Molding Shrinkage - Flow | 0.20 - 0.50 | % | |
| Water Absorption (Equilibrium) | 0.020 | % |
| Hardness | Nominal Value | Unit | |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 |
| Mechanical | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength | 140 | MPa | |
| Tensile Elongation (Break) | 1.6 | % | |
| Flexural Modulus | 17000 | MPa | |
| Flexural Strength | 210 | MPa | |
| Compressive Strength | 140 | MPa |
| Impact | Nominal Value | Unit | |
|---|---|---|---|
| Notched Izod Impact | 8.00 | kJ/m² |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 265 | °C | |
| Melting Temperature | 285 | °C | |
| CLTE - Flow | 1.8E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | |
|---|---|---|---|
| Surface Resistivity | 1.0E+6 - 1.0E+10 | ohms | |
| Volume Resistivity | 1.0E+7 - 1.0E+11 | ohms·cm |
| Flammability | Nominal Value | Unit | |
|---|---|---|---|
| Flame Rating (2.0 mm) | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 140 | °C | |
| Drying Time | 4.0 - 8.0 | hr | |
| Rear Temperature | 240 - 260 | °C | |
| Middle Temperature | 290 - 310 | °C | |
| Front Temperature | 300 - 330 | °C | |
| Mold Temperature | 100 - 140 | °C | |
| Injection Rate | Moderate | ||
| Back Pressure | 60.0 - 80.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resinoid 2010 | Resinoid Engineering Corporation | Phenolic | Resinoid |
| SHIN-A SE-650 | SHIN-A T&C | Epoxy | SHIN-A |
| BP PPC 0510 BLK | Buckeye Polymers, Inc. | PP Copolymer | BP |
| ISPLEN® PP 099 X2M | REPSOL | PP Homopolymer | ISPLEN® |
| SIBUR Synthetic Rubber NBR 2645 | SIBUR | NBR | SIBUR Synthetic Rubber |