Latene® 7H2W T-V0E
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xZYuiB_Latene-7H2W-T-V0E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polypropylene homopolymer (PPh). Heat and metal stabilised. Mineral filler. UL94 V-0 classified, with halogens, PBB/PBDE free. Product UL certified. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.32 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.70 to 0.90 | % | |
| Flow : 2.00 mm | 0.75 to 0.95 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 3500 | MPa | |
| 60°C | 1450 | MPa | |
| 90°C | 1000 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 25.0 | MPa | |
| Yield, 60°C | 17.0 | MPa | |
| Yield, 90°C | 12.0 | MPa | |
| Break, 23°C | 25.0 | MPa | |
| Break, 60°C | 15.0 | MPa | |
| Break, 90°C | 10.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 2.3 | % | |
| Yield, 60°C | 6.0 | % | |
| Yield, 90°C | 7.0 | % | |
| Break, 23°C | 3.7 | % | |
| Break, 60°C | 6.0 | % | |
| Break, 90°C | 10 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 2.3 | kJ/m² | |
| 23°C | 2.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 6.5 | kJ/m² | |
| 23°C | 20 | kJ/m² | |
| Notched Izod Impact (23°C, 3.20 mm) | 25 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 115 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 105 | °C | |
| Vicat Softening Temperature | 70.0 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 4.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index 3(Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | 5VB | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 2.00 mm | 960 | °C | |
| Oxygen Index | 27 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 180 to 220 | °C | |
| Mold Temperature | 20.0 to 40.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| 3 . | Without Surfactant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD C 101 HF | RTP Company | PP, Unspecified | RTP |
| Sylvin 7868-95C Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Multiuse Leostomer® LJ-3170N | Riken Technos Corp. | TPU, Unspecified | Multiuse Leostomer® |
| FERREX® GPP30CS74UL BLUE | Ferro Corporation | PP Copolymer | FERREX® |
| Hipolyene X2 DP 4 | Zylog Plastalloys | TPO (POE) | Hipolyene |