Polypropylene DGF080.00 ESU
| Category: | TPO , Developmental Performance Polymers |
| Manufacturer: | Trinseo |
| Trademark: | Polypropylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xZIK7Q_Polypropylene-DGF080-00-ESU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.980 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 60 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 21.6 | MPa | ISO 527-2 |
| Flexural Modulus | 1400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 6.0 | kJ/m² | |
| 23°C | 17 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 95.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 52.0 | °C | ISO 75-2/Af |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 1 | 35 | mm/min | ISO 3795 |
| Note Message | |
|---|---|
| 1 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROMID A 280 Z3 | Taro Plast S.p.A. | Nylon 66 | TAROMID A |
| Celcon® LM90Z | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |
| Daicel PP PTS4N1 | Daicel Polymer Ltd. | PP, Unspecified | Daicel PP |
| Pebax® Rnew 80R53 SP 02 | Arkema | PEBA-Ether | Pebax® Rnew |
| Braskem PP CSP120NA | Braskem America Inc. | PP Impact Copolymer | Braskem PP |