Andur 6 DPLM/Curene® 442
| Category: | PUR-Ester/TDI , Polyurethane (Polyester, TDI) |
| Manufacturer: | Anderson Development Company |
| Trademark: | Andur |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xZ3Ob8_Andur-6-DPLM-Curene-442.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Andur 6-DP-LM is a polyester based, toluene diisocyanate terminated prepolymer. An elastomer with a hardness of 60 Shore D is obtained when this prepolymer is cured with Curene 442 [4,4'-methylene-bis (orthochloroaniline)]. Elastomers of lower hardness can be obtained by reaction with polyols and their combination with Curene 442 and other diamines, or through the use of plasticizers. |
| General Information | |
|---|---|
| Forms |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore D) | 61 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Strength | ASTM D695 | ||
| 5% strain | 1.91 | MPa | ASTM D695 |
| 10% strain | 7.82 | MPa | ASTM D695 |
| 15% strain | 12.6 | MPa | ASTM D695 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 19.7 | MPa | ASTM D412 |
| 300% strain | 38.4 | MPa | ASTM D412 |
| Tensile Strength (Yield) | 56.7 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 400 | % | ASTM D412 |
| Compression Set | 35 | % | ASTM D395B |
| Bayshore Resilience | 44 | % | ASTM D2632 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Pot Life | 3.0 | min | |
| Demold Time | 30 | min | |
| Post Cure Time (96°C) | 16 | hr |
| Additional Information |
|---|
| Durometer Hardness, ASTM D2240, Shore D: 58 to 63Die C Tear, ASTM D1004: 705 pliAverage Split Tear, ASTM D1938: 422 pliStoichiometry Curative Level: 95%Mix Temperature: Andur 6 DPLM: 158-180°F Curene 442: 230-250°F |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 104 - 113 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® Homo 18.F | Marco Polo International, Inc. | PP Homopolymer | MARPOL® Homo |
| Tuffak® S | Altuglas International of Arkema Inc. | PC | Tuffak® |
| ACCUTECH™ ABS892EV | ACLO Compounders Inc. | ABS | ACCUTECH™ |
| Bamtac BPP035A | Ningbo Bamtac New Material Col, Ltd. | PP, Unspecified | Bamtac |
| IPC PP 4820H-C | International Polymers Corporation | PP Homopolymer | IPC PP |