MAJORIS DFR167
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xYXfVU_MAJORIS-DFR167.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DFR167 is a low halogen flame retardant compound UL 94 V2, intended for injection moulding. The product is available in natural (DFR167) but other colours can be provided on request DFR167 produce very low level of toxicity and low smoke density in the case of a fire. The product is UV stabilised and antistatic. Provides an excellent balance of high impact strength and rigidity. DFR167 is especially designed for electrical and seats exterior applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.978 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 69 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 25.0 | MPa | ISO 527-2/50 |
| Fracture | 7.00 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 9.0 | % | ISO 527-2/50 |
| Fracture | 200 | % | ISO 527-2/50 |
| Flexural Modulus - 1% Secant | 1250 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 5.0 | kJ/m² | ISO 179/1eA |
| 23°C | 14 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 3.0 | kJ/m² | ISO 180/1A |
| 23°C | 14 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 87.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 45.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 144 | °C | ISO 306/A |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-2 | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 850 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 210 - 240 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Talcoprene® 1522SMT NERO | SO.F.TER. SPA | PP Homopolymer | Talcoprene® |
| Tarnoform® 300 K | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| PARAPET GR01270 | Kuraray Co., Ltd. | Acrylic (PMMA) | PARAPET |
| Sumiliteresin® PR-3700 I | SBHPP | Phenolic | Sumiliteresin® |
| Delene 3570 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TPE | Delene |