LNP™ THERMOCOMP™ JF002R compound
| Category: | PESU , Polyethersulfone |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xYHSE5_LNP-THERMOCOMP-JF002R-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP JF002R is a compound based on Polyethersulfone resin containing Glass Fiber, Glass Bead. Added features of this material include: Mold Release. Also known as: LNP* THERMOCOMP* Compound JF-1002 MG MR Product reorder name: JF002R |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.45 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3500 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 83.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Yield) | 4.5 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 3200 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| -- 3 | 133 | MPa | |
| -- 4 | 74.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 5(23°C) | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 6(23°C) | 45 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 7 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 221 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 212 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 4.3E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 5.5E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Yield |
| 4 . | Break |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYTROPE® STR 3567EU-01 CLEAR | A. Schulman Inc. | Polyolefin, Enhanced (Capstock Resin) | POLYTROPE® |
| Quadrant EPP Acetron® GP Acetal | Quadrant Engineering Plastic Products | Acetal (POM) Copolymer | Quadrant EPP |
| Daelim Po1y® LL-24W | DAELIM INDUSTRIAL CO., LTD. | LLDPE | Daelim Po1y® |
| PENTAMID B GV15 H RC schwarz | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |
| Sylvin 916VO-90 Grey 9565 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |