Dynaflex™ D3226-1000-03
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Dynaflex™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xY9NHe_Dynaflex-D3226-1000-03.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Dynaflex™D3226-1000-03 is an easy-to-process TPE designed for general-purpose applications. It is suitable for injection molding, extrusion molding, blow molding and thermoforming processes.
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.988 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 26 | g/10 min | ASTM D1238 |
| 200°C/5.0 kg | 82 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 - 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 10 sec) | 40 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain, 23°C) | 2.96 | MPa | ASTM D412 |
| Tensile Strength (Break, 23°C) | 3.59 | MPa | ASTM D412 |
| Tensile Elongation (Break, 23°C) | 380 | % | ASTM D412 |
| Tear Strength | 15.8 | kN/m | ASTM D624 |
| Compression Set (23°C, 22 hr) | 15 | % | ASTM D395B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 154 - 193 | °C | |
| Middle Temperature | 160 - 199 | °C | |
| Front Temperature | 166 - 204 | °C | |
| Nozzle Temperature | 166 - 204 | °C | |
| Mold Temperature | 21.1 - 32.2 | °C | |
| Back Pressure | 0.345 - 1.03 | MPa | |
| Screw Speed | 25 - 75 | rpm |
| Injection instructions |
|---|
| 以乙烯醋酸乙烯共聚物 (EVA) 为基础的色母料最适合 Dynaflex™ D3226-1000-03 着色。使用熔体流动速率较高（范围为 25 - 40 克/10 分钟）的色母料，则能达到较好的颜色分散效果（一致性）。典型的色母料用量为 1% 至 5%（重量）。若使用 GLS 可供的预着色复合材料，则可达到较好的配色一致性。不应采用以 PVC 为基础的色母料。色母料是否适用，应由用户通过试验来最终确定。在使用此产品之前或之后，均须用熔体流动速率较低 (0.5 - 2.5 MFR) 的聚苯乙烯 (PS) 或聚丙烯 (PP) 彻底进行置换。Dynaflex™ D3226-1000-03 具有良好的熔体稳定性。最长停留时间可能会根据机筒尺寸有所变化。通常，如果机器闲置 5 - 8 分钟或以上，则应将机筒排空。不需要干燥注射速度：1 - 5 英寸/秒第一阶段 - 提升压力：200 - 600 psi第二阶段 - 保持压力：70% 的升压保持时间（厚部件）：4 - 10 秒保持时间（薄部件）：1 - 3 秒 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SOLPLAST TH 8000D | UTEKSOL d.o.o. | SBS | SOLPLAST TH |
| VINIKA® CB70KA | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | VINIKA® |
| ACCUTECH™ CP0436G10M20CL | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| Sylvin 8354-62D Yellow 4193 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 7833-70 White 1348 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |