Order Products : sales@su-jiao.com
Karina BLUE COLOR CONCENTRATE 06/595-FC-LMP
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Karina Ind. e Com. de Plásticos Ltda |
| Trademark: | Karina |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xWdkcq_Karina-BLUE-COLOR-CONCENTRATE-06-595-FC-LMP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HEAVY METAL FREE COLOR CONCENTRATE RECOMMENDED FOR APPLICATION IN ELECTRICAL WIRE AND CABLE PVC COMPOUNDS. ALSO SUITABLE FOR PIGMENTATION OF FLEXIBLE AND RIGID PVC COMPOUNDS FOR GENERAL PURPOSES. RECOMMENDED TO USE 2%. |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.35 to 1.41 | g/cm³ | ASTM D792 |
| Cadmium Content | < 50 | ppm | IEC 62321 |
| Chromium Content | < 100 | ppm | IEC 62321 |
| Color | OK | ME 12 | |
| Color a | -19.7 to -16.7 | ME 12 | |
| Color b | -35.4 to -32.4 | ME 12 | |
| Color L | 62.8 to 65.8 | ME 12 | |
| Mercury Content | < 100 | ppm | IEC 62321 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bromine Content | < 100 | ppm | IEC 62321 |
| Lead Content | < 100 | ppm | IEC 62321 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 80 to 84 | ASTM D2240 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 2 | > 1.0E+14 | ohms·cm | ASTM D257 |
| Note Message | |
|---|---|
| 1 . | 24 hr |
| 2 . | 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prixene® EA080I65 | POLYMAT | HDPE | Prixene® |
| XENOY™ 1760T resin | SABIC Innovative Plastics Europe | PC+PBT | XENOY™ |
| Fainplast EVA 801S | Fainplast Compounds S.r.l | EVA | Fainplast |
| DOWLEX™ 2037 | The Dow Chemical Company | LLDPE | DOWLEX™ |
| KYOCERA KE-G3000DA | KYOCERA Chemical Corporation | Epoxy | KYOCERA |