Mecoline IS RDX 1232 F
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | Melos GmbH |
| Trademark: | Mecoline |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xWA5Fn_Mecoline-IS-RDX-1232-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This compound with extra low temperature resistance and extra oil resistance is classified as hazard level 4 identification code M. It is an excellent choice for compact wiring systems, where a reduced wall thickness results in space and weight savings |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/10.0 kg) | 3.9 | g/10 min | ISO 1133 |
| Water Absorption - after 168h at 70°C | < 15.0 | mg/cm² | |
| pH | > 4.5 | IEC 60754-2 | |
| Shrinkage - 1h at 120°C | < 2.0 | % | IEC 811-1-3 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hot Pressure Test - penetration 4h at 140°C | < 50 | % | DIN VDE 0472 |
| Hot Set 1 | IEC 540 | ||
| Elongation under load | < 60 | % | |
| Residual elongation | < 10 | % | |
| Temperature Index | 250 | °C | ASTM D2863 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Conductivity | < 4.00 | µS/mm | EN 50267-2-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Halogen Content | 0 | % | IEC 754-1 |
| Toxicity | 2.60 | EN 50305 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 155 to 165 | °C | |
| Extruder Screw L/D Ratio | >25.0:1.0 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 50 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | IEC 811-1-1 | ||
| -- 2 | > 16.0 | MPa | |
| -- 3 | > 15.0 | MPa | |
| Tensile Strain | |||
| Break 4 | > 150 | % | IEC 811-1-1 |
| Break 5 | > 200 | % | IEC 811-1-1 |
| Break, -40°C | > 30 | % | IEC 811-1-4 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (120°C, 240 hr) | < 25 | % | IEC 811-1-2 |
| Change in Tensile Strain at Break in Air (120°C, 240 hr) | < 25 | % | IEC 811-1-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | IEC 60093 | ||
| 23°C | 1.0E+15 | ohms·cm | |
| 90°C | < 1.0E+12 | ohms·cm |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 32 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 130 to 140 | °C | |
| Cylinder Zone 2 Temp. | 140 to 150 | °C | |
| Cylinder Zone 3 Temp. | 150 to 160 | °C | |
| Cylinder Zone 4 Temp. | 155 to 165 | °C | |
| Cylinder Zone 5 Temp. | 155 to 165 | °C | |
| Adapter Temperature | 155 to 165 | °C | |
| Die Temperature | 160 to 170 | °C |
| Note Message | |
|---|---|
| 1 . | at 200°C/15min/0.2 MPa |
| 2 . | After crosslinking |
| 3 . | Before crosslinking |
| 4 . | After crosslinking |
| 5 . | Before crosslinking |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU P190 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Borealis PP TR529 | Borealis AG | PP, Unspecified | Borealis PP |
| ECONAMID® 6ST1 | DOMO Engineering Plastics SPA | Nylon 6 | ECONAMID® |
| Hanwha Total PE 532L | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | LDPE | Hanwha Total PE |
| TORZEN® G3300L NC01 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |