PELPRENE™ S6002 is a Thermoplastic Polyester Elastomer (TPEE) product. It is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (2.00 mm) | 1.7 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 65% RH) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| Shore A | 99 | JIS K6301 | |
| Shore D | 72 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| -- | 46.0 | MPa | |
| 50% Strain | 27.5 | MPa | |
| Tensile Elongation (Break) | 450 | % | ASTM D638 |
| Flexural Modulus | 568 | MPa | ASTM D790 |
| Compressive Strength (10% Strain) | 30.8 | MPa | ASTM D695 |
| Taber Abrasion Resistance (1000 Cycles) | 8.00 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | 196 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 200 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 130 | °C | ASTM D648 |
| Brittleness Temperature | -60.0 | °C | JIS K6301 |
| Vicat Softening Temperature | 202 | °C | ASTM D1525 |
| Melting Temperature | 218 | °C | DSC |
| CLTE - Flow | 1.4E-4 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 5.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 30 | kV/mm | JIS K2111 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Resilience | 56 | % | JIS K6301 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadraflex™ ALE-95A-B30 | Biomerics, LLC | TPU-Polyether | Quadraflex™ |
| TRIMID® N66-G33 | Polymer Technology and Services, LLC | Nylon 66 | TRIMID® |
| Evermore PUR UDA-10XT | Evermore Chemical Industry Co., Ltd. | PUR-Ether | Evermore PUR |
| OTECH PVC OE8836 - Profile | OTECH Corporation | PVC, Unspecified | OTECH PVC |
| Sylvin 8915-90 UV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |